Weather Resistant HDPE Smooth Geomembrane For Various Applications
Product Introduction
Smooth geomembrane, also known as smooth geomembrane, is a widely
used waterproof barrier geosynthetic material. The material is
based on high polymer, with extremely low permeability, excellent
chemical resistance and ultraviolet resistance, and has a high cost
performance. The smooth geomemofilm uses high quality primary high
density polyethylene (HDPE) as the impermeable substrate. Carbon
black, antioxidant, anti-aging agent, ultraviolet absorber and
color masterbatch are added in the production process. It is
prepared by three layer co-extrusion blow molding technology.
Product Properties
The smooth geomembrane has the advantages of high impermeability,
high tensile strength, good flexibility, flexibility and so on. It
can adapt to the geological uneven settlement, and has excellent
chemical corrosion resistance and weather resistance. In addition,
the smooth geomembrane also has good heat resistance and cold
resistance. It also has resistance to ultraviolet radiation and
good anti-aging properties, suitable for long-term use.
Product Application
Smooth geomembrane has been widely used in many fields because of
its unique properties. For example, in water conservancy projects,
it can be used for anti-seepage treatment of river dikes, lake
DAMS, tailings DAMS, etc. In municipal engineering, it can be used
for anti-seepage lining of subway and underground engineering of
buildings. In addition, it is also suitable for aquaculture,
landscape engineering, salt industry, transportation
infrastructure, petrochemical industry and mining engineering and
other fields.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density (g/c㎡,≥) | 0.939 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 700 | |
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| Density (g/c㎡,≥) | 0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | |
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | |
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | |
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | |
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | |
| Carbon Black Content (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not
allowed | |