Seamless HDPE Smooth Geomembrane For Effective Seepage Control
Product Introduction
Smooth geomembrane, also known as smooth geomembrane, is a kind of
waterproof barrier geosynthetic material with high polymer as the
basic raw material. It is made of high quality primary high density
polyethylene (HDPE) as impermeable substrate, adding carbon black,
antioxidant, anti-aging agent, ultraviolet absorber and color
masterbatch through special formula, and using three-layer
co-extrusion blow molding technology. This material has very low
permeability, excellent chemical resistance and UV resistance
properties, and cost-effective, is the first choice of civil
engineering seepage prevention materials, widely used in many
fields.
Product Properties
1. Environmental protection: does not contain harmful substances,
do not pollute the environment.
2. Reusability: Only the surface layer can be replaced, saving
resources.
3. Wide range of application: suitable for basement, pool and other
types of waterproof projects.
4. Uv resistance: Protects the material from UV damage.
5. Good stability: it is not easy to deform or break under physical
action.
Product Application
1. Water conservancy: can be used for seepage, drainage, protection
and so on.
2. Environmental protection: suitable for landfills, sewage
treatment plants, etc.
3. Municipal engineering: can be used for waterproofing and
protection of underground facilities.
4. Aquaculture: Used for seepage prevention of fish ponds, shrimp
ponds, etc.
5. Sewage treatment: applied in tailings seepage prevention and
landfill.
6. Landscape: provides beauty while ensuring water resistance.
7. Hydraulic engineering: plays a role in the seepage prevention of
DAMS and reservoirs.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density (g/c㎡,≥) | 0.939 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 700 | |
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| Density (g/c㎡,≥) | 0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | |
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | |
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | |
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | |
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | |
| Carbon Black Content (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not
allowed | |