Chemical Resistant HDPE Smooth Geomembrane For Environmental
Protection
Product Introduction
Smooth geomembrane, also known as smooth geomembrane, is a widely
used waterproof barrier geosynthetic material. The material is made
of high polymer as the basic raw material, by using high quality
primary high density polyethylene (HDPE) as the impermeable
substrate, adding a certain amount of carbon black, antioxidant,
anti-aging agent, ultraviolet absorber and color masterbatch in the
production process, and by three layer co-extrusion blow molding
technology batch refining.
Product Properties
High tensile strength, high tear resistance, good flexural,
flexibility, elasticity, adapt to geological uneven settlement,
strong acid, alkali, oil corrosion resistance, excellent chemical
corrosion resistance, good heat resistance and cold resistance.
Product Application
1. Water conservancy project: including river dike, lake dam,
tailings dam, sewage dam and reservoir area, water channel, liquid
storage tank, etc.
2. Environmental protection engineering: such as landfill, sewage
treatment plant, power plant regulating pond and other waste
treatment site seepage prevention.
3. Municipal engineering: subway, building underground engineering,
planting roof, roof garden, sewage pipe, etc.
4 Aquaculture: Suitable for seawater and freshwater fish and shrimp
farms.
5. Landscape engineering: waterproofing and moisture-proof of
river, reservoir, artificial lake, pond bottom of golf course,
slope protection and green lawn.
6. Salt industry: salt field crystallization pool, halogen pool
cover, salt film, salt pool plastic mat film, etc.
7. Transportation infrastructure: roads, highways, railway
foundation waterproof layer, etc.
8. Petrochemical industry: chemical plants, refineries, oil storage
tank impermeability, chemical reaction tank, sedimentation tank
lining, etc.
9. Mining engineering: the bottom lining of washing pool, pile
leaching pool, ash pile, dissolution pool, sedimentation tank, pile
yard, tailings and so on.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density (g/c㎡,≥) | 0.939 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 700 | |
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| Density (g/c㎡,≥) | 0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | |
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | |
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | |
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | |
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | |
| Carbon Black Content (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not
allowed | |