Anti-Skid HDPE Textured Geomembrane For Enhanced Stability On Steep
Slopes
Product Introduction
As a kind of geotechnical material with special surface structure,
the design of cylindrical rough surface geomembrane aims to improve
its anti-skid performance and adhesion to soil or other materials.
Product Properties
1. High coefficient of friction: The column point design
significantly increases the friction coefficient of the
geomembrane, giving it better stability on steep or vertical
slopes.
2. Good impermeable performance: Inherited the excellent
impermeable characteristics of HDPE geomemofilm, effectively
preventing the penetration of water and pollutants.
3. Enhanced adhesion: The column point structure improves the
adhesion of the geomembrane to the soil, helping to prevent sliding
of the geomembrane on slopes.
4. Chemical resistance: It has good resistance to most chemical
substances and is suitable for use in a variety of environments.
5. Resistance to environmental stress cracking: It can remain
stable in harsh environments and is not easy to crack.
6. Temperature adaptability: can be used in a wide temperature
range, with good heat resistance and cold resistance.
Product Application
1. Steep slope seepage prevention project: column point rough
surface geomembrane is especially suitable for steep slope seepage
prevention project, improve the stability of the project.
2. Vertical impermeability: In vertical or near-vertical
impermeability projects, the column point design helps to keep the
geomembrane fixed.
3. Dam reinforcement: used for dam reinforcement engineering,
improve the stability of the dam and anti-seepage performance.
4. Landfill: It is used in the slope anti-slip and anti-seepage of
landfill and sealed field to prevent pollutants from penetrating
into the environment.
Products series
Single textured geomembrane, double-wall textured geomembrane.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width: 4m~8m
* Roll length: 50m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (GB/T 17643-2011(GH-2T1,GH-2T2))
| Serial Number | Project | Index | | Thickness(mm) | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | | 1 | Density (g/c㎡,≥) | ≥0.940 | | 2 | Textured Highth (mm) | ≥0.25 | | 3 | Yield Strength (N/mm,LD/TD) | ≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 | | 4 | Breaking Strength (N/mm,LD/TD) | ≥8 | ≥10 | ≥13 | ≥16 | ≥21 | ≥26 | ≥32 | | 5 | Yeild Elongation Rate (%) | ≥12 | | 6 | Breaking Elongation Rate (%) | ≥100 | | 7 | Rectangular Tear Strength (N) | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 | | 8 | Puncture Strength (N) | ≥200 | ≥270 | ≥335 | ≥400 | ≥535 | ≥670 | ≥800 | | 9 | Tensile Load Stress Cracking (Notch Constant Load Tensle Method) h | ≥300 | | 10 | Carbon Black Content(Rang) (%) | 2.0~3.0 | | 11 | Carbon Black Dispersion | There is not more than one grade 3 in 10 data, and grade 4 and
grade 5 are not allowed | | 12 | Oxidative Induction Time (OIT) | Standard OIT (min)≥100 | | High Pressure OIT (min)≥400 | | 13 | 85℃ thermal aging (Atmospheric Pressure OIT Retention After 90 Day) | ≥55 | | 14 | Ultraviolet Irradiation After 1600 Hours, The OIT Retention(%) | ≥50 |
|
(CJ-T234-2006)
| Specification | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Textured Highth (mm) | 0.25 | |
| Density (g/c㎡,≥) | 0.94 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 10 | 13 | 16 | 21 | 26 | 32 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 100 | |
| Rectangular Tear Strength (N) | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 267 | 333 | 400 | 534 | 667 | 800 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |