Customizable HDPE Textured Geomembrane for Tailings Storage and
Landfill Applications
Product Introduction
Column point geomembrane is a type of impermeable material made
from high molecular polymer as the basic raw material. It not only
prevents liquid seepage but also prevents gas volatilization. This
material has a wide range of applications in construction
engineering, highway tunnels, subways, railway tunnels, industrial
and mining, and municipal underground engineering projects.
Product Properties
The characteristics of the pillar point geomembrane lie in its
surface pillar point structure, which is formed by a special mold
pressing roller, evenly distributed, both beautiful and capable of
increasing the friction coefficient. The front and back sides of
the membrane can be hot-fused into one with different materials and
colors, allowing the product's front and back sides to be set
according to geological conditions and engineering requirements in
engineering applications. This production process not only retains
the mechanical properties of the material itself, as well as good
elongation and chemical property stability, but also enhances the
product's tensile, wear resistance, and puncture resistance through
the addition of a certain proportion of functional additives. In
addition, the pillar point geomembrane has a high resistance to
acid and alkali, microbial, and chemical erosion.
Product Application
1. Landfill: Used as an impermeable layer to prevent contaminants
from seeping into groundwater.
2. Tailings storage yard: prevent harmful substances in tailings
from penetrating into the environment.
3. Slope engineering: Due to its high friction, it is particularly
suitable for slope engineering to prevent geomembrane from sliding.
4. Dam anti-seepage: enhance the anti-seepage capacity of the dam
to prevent water penetration.
5. Artificial lakes and reservoirs: as impermeable layers, maintain
the stability of water bodies.
Products series
Single textured geomembrane, double-wall textured geomembrane.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width: 4m~8m.
* Roll length: (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (GB/T 17643-2011(GH-2T1,GH-2T2))
| Serial Number | Project | Index | | Thickness(mm) | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | | 1 | Density (g/c㎡,≥) | ≥0.940 | | 2 | Textured Highth (mm) | ≥0.25 | | 3 | Yield Strength (N/mm,LD/TD) | ≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 | | 4 | Breaking Strength (N/mm,LD/TD) | ≥8 | ≥10 | ≥13 | ≥16 | ≥21 | ≥26 | ≥32 | | 5 | Yeild Elongation Rate (%) | ≥12 | | 6 | Breaking Elongation Rate (%) | ≥100 | | 7 | Rectangular Tear Strength (N) | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 | | 8 | Puncture Strength (N) | ≥200 | ≥270 | ≥335 | ≥400 | ≥535 | ≥670 | ≥800 | | 9 | Tensile Load Stress Cracking (Notch Constant Load Tensle Method) h | ≥300 | | 10 | Carbon Black Content(Rang) (%) | 2.0~3.0 | | 11 | Carbon Black Dispersion | There is not more than one grade 3 in 10 data, and grade 4 and
grade 5 are not allowed | | 12 | Oxidative Induction Time (OIT) | Standard OIT (min)≥100 | | High Pressure OIT (min)≥400 | | 13 | 85℃ thermal aging (Atmospheric Pressure OIT Retention After 90 Day) | ≥55 | | 14 | Ultraviolet Irradiation After 1600 Hours, The OIT Retention(%) | ≥50 |
|
(CJ-T234-2006)
| Specification | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Textured Highth (mm) | 0.25 | |
| Density (g/c㎡,≥) | 0.94 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 10 | 13 | 16 | 21 | 26 | 32 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 100 | |
| Rectangular Tear Strength (N) | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 267 | 333 | 400 | 534 | 667 | 800 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |