Black and Green Dual-color HDPE Smooth Geomembrane Suitable for
Various Waterproof Projects
Product Introduction
The black and green dual-color HDPE geomembrane is a high-density
polyethylene (HDPE) or low-density polyethylene (LLDPE) material
formed through double-layer co-extrusion blow molding. It is
characterized by its two sides, one black and the other green. This
design gives it a wide range of applications in various fields.
Product Properties
1. Environmental protection: does not contain harmful substances,
do not pollute the environment.
2. Reusability: Only the surface layer can be replaced, saving
resources.
3. Wide range of application: suitable for basement, pool and other
types of waterproof projects.
4. Uv resistance: Protects the material from UV damage.
5. Good stability: it is not easy to deform or break under physical
action.
Product Application
Landfill Cover: The green side is up, mainly for aesthetic and environmental
purposes. It also has anti-aging and light stability properties,
with a lifespan of more than five years.
Slope Covering: Prevents rainwater from seeping into the landfill, increasing its
service life and reducing the cost of leachate treatment.
Tailings Pond Covering: Utilizing the aesthetic and environmental benefits of the green
side, while the black side faces down to effectively prevent
moisture penetration.
The black and green dual-color HDPE geomembrane has been widely
used in multiple engineering projects, including but not limited to
canal renovation, artificial lakes, water conservancy construction
projects, etc. In particular, its excellent impermeability and
convenient construction have been widely recognized in channel
seepage prevention projects.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density (g/c㎡,≥) | 0.939 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 700 | |
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| Density (g/c㎡,≥) | 0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | |
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | |
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | |
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | |
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | |
| Carbon Black Content (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not
allowed | |